VAE Emulsion DA102H glue

具体地点:向阳街道 微信号:18615956809 联系人:李连慰 Dairen Chemical Corporation VAE Emulsion DA-102H PRODUCT SPECIFICATIONS Inspection Method Value Solids content: DCC method 55 % min. Viscosity at 25 °C : DCC method 3500 - 4500 mPa.s Ph: DCC method 4.5- 6.5 TYPICAL PROPERTY Inspection Method Value Film Appearance: DCC method Clear, glossy Tg: DCC method 0 ℃ Stabilizing System: DCC method Polyvinyl Alcohol INTRODUCTION DA-102H is a non-plasticized aqueous milky white copolymer dispersion based on vinyl acetate and ethylene. After evaporation of its water content, DA-102H forms a flexible film with best adhesive properties for broad applications. In generally, DA-102H is used as general adhesive for packaging, bookbinding, and bonding for plastic films, coated papers. Furthermore, DA-102H is broadly used as a particularly suitable base emulsion for the formulation of adhesives for difficult substrates, such as lacquered surfaces, foils and plastic films in the packaging and paper industry. DA-102H is also an excellent base emulsion for floor-, wall- or ceiling adhesives. It shows good resistance against aging, light or saponification. As a result, the durability of your products could be enhanced with usage of DA-102H and suitable applicative industrial formulations. Besides, DA-102H is very friendly product for our environment. From the viewpoint of industrial applications, the compatibility of raw materials is considered important to manufacturers. Compatibility with different tackifiers, plasticizers, solvents and extenders is generally good, although this has to be checked in each individual case of course. RECOMMENDED APPLICATIONS As mentioned before, DA-102H provides a soft and flexible film to porous and non porous substrates of all kind of common plastic materials. If at least one substrate is porous, aqueous formulations can be used for directly bonding the substrates, while plastic/plastic, film/film or film/lacquered surfaces afford application of the emulsion (or its formulation) onto one substrate and intermediately drying, followed by sealing the other non-polar substrate. Depending on the machinery, of course such a sealing process could be used also bonding non-polar substrates to polar ones. The popular use of DA-102H is for bonding difficult substrates, like -plastic- (specially PVC-) or metal films to substrates of all kind -printed paper, lacquered paper and board -plastic materials to porous or even non-porous substrates -ceramic tiles to cementitious substrates As DA-102H is compatible with cement, we can reinforce waterproofing capability of cementitious compounds formulated with our product. SAFETY & STORAGE In general, DA-102H is considered safe for its intended use. However, as this class of products always contains minor amount of residual vinyl acetate monomer, adequate ventilation is recommended in rooms where DA-102H is handled. Generally when working with polymer emulsions, protective clothes, gloves and also goggles should be used. Splashes on the skin or in the eyes should immediately be removed by irrigation with clean water. DA-102H should be stored in sheltered areas at temperatures between 5 and 40 ℃; do never store under freezing conditions. Opened containers should be closed soon to prevent skinning. It is recommended to use the emulsion within 6 months. Finished products manufactured from polymer emulsions usually also require preservation.